Structural evolution of Ni-20Cr alloy during ball milling of elemental powders Structural evolution of Ni-20Cr alloy during ball milling of elemental powders |
| Autores: |
López-Báez, I. Martínez-Franco, E. Zoz, H. Trápaga-Martínez, L. G. |
| Fecha: | 2011-05-23 |
| Publicador: | Revistas UNAM |
| Fuente: |
 |
| Tipo: |
|
| Tema: |
Mechanical alloying; solid solubility; X-ray diffraction; metastability; lamellar refinement Aleado mecánico; solubilidad sólida; difracción de rayos-X; metaestabilidad; refinamiento laminar |
| Descripción: |
The ball milling (BM) of blended Ni and Cr elemental powders was carried out in a Simoloyer performing on high-energy scale mode at maximum production to obtain a nanostructured Ni-20Cr alloy. The phase transformations and structural changes occurring during mechanical alloying were investigated by X-ray diffraction (XRD) and optical microscopy (OM). A gradual solid solubility of Cr and the subsequent formation of crystalline metastable solid solutions described in terms of the Avrami-Erofe’ev kinetics model were calculated. The XRD analysis of the structure indicates that cumulative lattice strain contributes to the driving force for solid solution between Ni and Cr during BM. Microstructure evolution has shown, additionally to the lamellar length refinement commonly observed, the folding of lamellae in the final processing stage. OM observations revealed that the lamellar spacing of Ni rich zones reaches a steady value near 500 nm and almost disappears after 30 h of milling. La molienda por bolas (MB) de la mezcla de polvos elementales Ni y Cr se realizó en un Simoloyer con una configuración de alta energía cinética y máxima capacidad de producción, el propósito fue obtener una aleación nanoestructurada Ni-20Cr. Las transformaciones de fase y los cambios estructurales llevados a cabo durante el aleado mecánico se investigaron utilizando las técnicas de difracción de rayos-X (DRX) y microscopía óptica (MO). Para el comportamiento cinético de la mezcla NiCr, pudo utilizarse el modelo cinético de Avrami-Erofe’ev para ajustar los datos experimentales de la solubilidad sólida del Cr y determinarse de esta manera un estado metaestable al aproximarse a la aleación Ni-20Cr. Los análisis de DRX indican que el almacenamiento de energía mecánica como deformación plástica contribuye con las fuerzas impulsoras para llevarse a cabo la solución sólida Ni(Cr) durante la MB. La evolución microestructural presentó un refinamiento adicional en la longitud de las laminillas concerniente a un doblamiento de las mismas en la etapa final del procesamiento. Las observaciones por MO revelaron que el espaciamiento laminar correspondiente a las zonas ricas en Ni alcanza un valor estable cercano a los 500 nm, y es casi despreciable después de 30 h de molienda. |
| Idioma: | Español |
1 Ordered Hunt Schemes for Overlaid CDMA Cellular Systems,Esquemas de ordenamiento en sistemas celulares sobrepuestos CDMA por Castañeda Camacho, J; Benemérita Universidad Autónoma de Puebla, Puebla, México,Lara Rodríguez, D; IPN | 6 Model for Adjustment of Aggregate Forecasts using Fuzzy Logic,Modelo para el ajuste de pronósticos agregados utilizando lógica difusa por Escobar Gómez, E N; Instituto Tecnológico de Tuxtla Gutiérrez Chiapas,Díaz Núñez, J J; Universidad Autónoma de Ciudad Juárez Chihuahua,Taracena Sanz, L F; Instituto Tecnológico de Querétaro, Querétaro |
2 Volatile Organic Compound Emissions from Light-Duty Vehicles During Cold-Starts,Emisiones de compuestos orgánicos volátiles durante arranques en frío de automóviles ligeros por Mendoza Domínguez, A; Tecnológico de Monterrey, Campus Monterrey, Nuevo León, México,León Romero, M A; Tecnológico de Monterrey, Campus Monterrey, Nuevo León, México,Caballero Mata, P | 7 Matrix Formulation of Foundations for Vibrating Machinery in Frequency Domain,Formulación matricial de cimentaciones para maquinaria vibratoria en el dominio de la frecuencia por Carbajal Romero, M F; Instituto Politécnico Nacional. México DF,Rodríguez Castellanos, A; Instituto Mexicano del Petróleo. México DF,Rodríguez Sánchez, J E; Instituto Mexicano del Petróleo. México DF,Flores Méndez, E; IPN |
3 Hydrogen Sorption Properties of the Intermetallic Mg2Ni Obtained by Using a Simoloyer Ball Milling,Propiedades de ab-desorción de hidrógeno del intermetálico Mg2Ni obtenido empleando un molino de bolas Simoloyer por Martínez Franco, E; IPN,Klassen, T; GKSS, Research Center Geesthacht, Germany,Jaramillo Vigueras, D; IPN,Bormann, R; GKSS, Research Center Geesthacht, Germany | 8 Numerical Approach to an Outflow Hydrograph of a Dambreak,Estimación numérica del hidrograma de salida de una presa debido a su ruptura por Fuentes Mariles, O A; Universidad Nacional Autónoma de México,Arganis Juárez, M L; UNAM,De Luna Cruz, F; UNAM,Franco, V; UNAM |
4 Electrical Parameters Extraction of CMOS Floating-Gate Inverters,Extracción de parámetros eléctricos de inversores CMOS de compuerta flotante por Molinar Solís, J E; Universidad Autónoma del Estado de México,Ponce Ponce, V H; IPN,García Lozano, R Z; Universidad Autónoma del Estado de México,Díaz Sanchez, A; Instituto Nacional de Astrofísica, Óptica y Electrónica INAOE,Rocha Pérez, j M; Instituto Nacional de Astrofísica, Óptica y Electrónica INAOE | 9 Back Work Ratio of Brayton Cycle,La relación de trabajo de retroceso de un ciclo Brayton por Malaver de la Fuente, M; Universidad Marítima del Caribe, Venezuela |
5 Active Rectifier with Extended Functions: An Option to Voltage Sags Ride Through and Power Quality Improvement,Rectificador activo con funciones ampliadas: una alternativa para la compensación de sags de voltaje y mejorar la calidad de la red eléctrica por Núñez Gutiérrez, C A; Universidad Autónoma de San Luis Potosí, SLP,Lira Pérez, J; Universidad Autónoma de San Luis Potosí, SLP,Pazos Flores, F; Universidad Autónoma de San Luis Potosí, SLP,Echavarría Solís, R; Universidad Politécnica de Victoria, Ciudad Victoria, Tamaulipas | 10 Flood Predictions Combining Regional and Single Site Hydrometric Information,Predicción de crecientes combinando información hidrométrica local y regional por Campos Aranda, D F; Universidad Autónoma de San Luis Potosí |