Título: |
Efecto de la clorhexidina en la resistencia microtensional de adhesivos autograbadores Effect of chlorhexidine on microtensile bond strength of self-etching adhesives |
Autores: |
Setién D., Víctor J. Bosetti, Yeresa Orellana, Noé Gregorio Ramírez, Robert Pable Pérez, Juan |
Fecha: |
2011-10-27 2011-10-27 2011-10-27 |
Publicador: | |
Fuente: |
Ver documento |
Tipo: | Texto |
Tema: |
Microtensión Adhesivo autograbador Resistencia tensional Clorhexidina Facultad de Odontología Microtensile bond strength Self-etching adhesive Clorhexidine Revista Odontológica de Los Andes: Trabajos de Investigación Revista Odontológica de Los Andes Medicina y Salud Revistas |
Descripción: |
El uso de adhesivos autograbadores se ha popularizado y el efecto de la clorhexidina antes de aplicarla no es conocido. Se propone determinar el efecto del
uso de gluconato de clorhexidina al 2% sobre dentina en la resistencia a la microtensión de dos adhesivos autograbadores: One Coat Bond 7.0, Coltene ® (OC)
y Futurabond NR, Voco® (FB). Para tal fin, se expuso una superficie plana de dentina de 16 molares humanos y se asignaron aleatoriamente a 4 grupos: Grupo
A (OC), Grupo B (OC) y clorhexidina, Grupo C (FB), y Grupo D (FB) y clorhexidina. Se colocó una capa de 4 milímetros de resina compuesta Filtek Z250 (3M
ESPE®) en incrementos de 2 mm, luego de 24 horas se obtuvieron 4 micro especímenes de 1 mm2 de cada diente y se probaron en tensión a 1 mm/min usando una
máquina de pruebas universales AGS-J Shimadzu. Los datos obtenidos fueron procesados en un programa SPSS 7.0 bajo un ANOVA y un test Tukey. La resistencia
promedio de cada grupo y la desviación estándar se muestran a continuación: Grupo A: 20.33 ± 6.9; Grupo B 14.21 ± 7.49; Grupo C 16.17 ± 6.65; Grupo D 10.05
± 7.32. La diferencias estadísticas (p=0.0015) entre los grupos se muestran como A>B y C>D. Los dos adhesivos autograbadores utilizados en este estudio
mostraron una disminución de sus fuerzas de unión cuando la dentina se trata previamente con clorhexidina al 2%, por lo que esta modalidad del procedimiento clínico debe ser utilizado con precaución. 16-22 vsetien@ula.ve noeorellana@yahoo.com The use of self-etching dental adhesives has become very practical and popular in dental practice; the effect of chlorhexidine prior bonding with them is not known. The objective was to determine the effect of chlorhexidine pretreatment on the micro-tensile bond strength (µTBS) of two different one-step self-etch dental adhesives, One Coat Bond 7.0, Coltene® (OC) and Futurabond NR, Voco® (FB). To this purpose was exposed flat oclusal dentine surface of 16 human molars were polished up to 320-grit silicon carbide paper. Teeth were assigned into 4 groups: Group a (OC), Group B (OC) + Chlorhexidine gluconate 2%, Group C (FB), and Group D (FB) + Chlorhexidine gluconate 2%. A 4-mm layer of Z250 hybrid composite applied in two increments. 4 micro-specimens samples were cut from each tooth. Micro-specimens were glued to two stiff acetate veneers and tested to failure in tension at 1 mm/min using a Shimadzu universal testing machine. Data was recorded in MPa and analyzed with ANOVA and Tukey post hoc test in SPSS software. Mean µTBS expressed in MPa and standard deviation (±SD) are shown here: Group A: 20.33 ± 6.9; Group B 14.21 ± 7.49; Group C 16.17 ± 6.65; Group D 10.05 ± 7.32. There was statistically significant difference (p=0.0015) among the groups, being A>B and C>D. The two one-step self-etch dental adhesives used in this study showed decrease in the bond strength when a 2% chlorhexidine treatment was applied prior to composite bonding thus such pretreatment should be used with caution with self-etch adhesives. |
Idioma: | Español |
1 Uso de materiales laminares tipo cobalto-molibdato como potenciales catalizadores en la transformación de limoneno por Salamanca, Maurin,Licea, Yordy,Echavarría, Adriana,Faro, Arnaldo,Palacio, Luz | 6 Tamices moleculares que combinan micro y meso porosidad: una revisión por López, Carmen M.,Sazo, Virginia,Urbina, Caribay,García, María G. |
2 | 7 Análisis y diseño sísmico por desempeño de edificios de muros estructurales por Monsalve Dávila, Jazmín T. |
3 | 8 |
4 Análisis por modelaje molecular del metoprolol y sus metabolitos por Lubes, Giuseppe | 9 Observatorio de Política Internacional IV. MUNDO GLOBAL - Mundo Global. Dos estadistas de película por Neira Fernández, Enrique |
5 Reducción catalítica selectiva de NOx usando nanopartículas de ferritas Cu1-XCoXFe2O4 como catalizador por Briceño, Sarah,Sagredo Arias, Vicente Segundo,Del Castillo Paredes, Hector Luis | 10 Introducción a la teoría espectral de los operadores no lineales por Appell, Jürgen |