| Título: | EFFECTS OF FORMING PROCESSING CONDITIONS ON THE FLEXURAL PROPERTIES OF BAGASSE AND BAMBOO PLASTIC COMPOSITES |
| Autores: | Shibata, Shinichi |
| Fecha: | 2012-08-06 |
| Publicador: | Bioresources |
| Fuente: |
 |
| Tipo: |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion |
| Tema: | Bagasse; Bamboo; Natural fiber; Composites; Processing conditions; Flexural modulus; Mechanical properties |
| Descripción: | The effects of processing conditions such as pressure, temperature, and holding time on the flexural properties of bagasse and bamboo biodegradable composites were investigated. Each sample of bagasse or bamboo was mixed with a corn-starch-based biodegradable resin and fabricated by a hot press forming method. The cross-sectional structure of the bagasse fiber was found to be porous and compressible, while that of bamboo was found to be more solid. The relationship between flexural strength, flexural modulus, and pressure in bagasse fiber was apparently different from that of bamboo due to the differences in the cross-sectional structure. In bagasse, the flexural strength and flexural modulus increased with the increase in pressure, whereas in bamboo those properties decreased. In bagasse, an increase in pressure made the fibers into a more compressed structure, increasing their flexural properties. In rigid bamboo, an increase in pressure caused the resin to extrude between fibers, and this resulted in lower flexural properties. At temperatures above 170 °C, the resin depolymerized thermally and the degree of polymerization decreased. Thus, the flexural modulus and strength decreased gradually with increase in holding temperature in both bagasse and bamboo composites. Furthermore, a maximum fiber volume fraction existed for both bagasse and bamboo plastic composites in the approximate range of 75% to 80%. |
| Idioma: | Inglés |