| Título: | INTERACTIONS BETWEEN CATIONIC POLYELECTROLYTE AND PULP FINES |
| Autores: |
Orblin, Elina Fardim, Pedro |
| Fecha: | 2011-04-29 |
| Publicador: | Bioresources |
| Fuente: |
 |
| Tipo: |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion |
| Tema: | Fines; Polyelectrolytes; XPS; ESCA; ToF-SIMS |
| Descripción: | Papermaking pulps are a mixture of fibres, fibre fragments, and small cells (parenchyma or ray cells), usually called pulp fines. The interactions between pulp fines and a cationic copolymer of acrylamide and acryloxyethyltrimethyl ammonium chloride were investigated based on solid-liquid isotherms prepared under different turbulence, and subsequent advanced surface characterization using X-ray photoelectron spectroscopy (XPS) and time-of-flight secondary ion mass spectrometry (ToF-SIMS). The surface charge and surface area of pulp fine substrates were measured by methylene blue sorption-XPS analysis and nitrogen adsorption combined with mercury porosimetry, respectively. The driving force behind polyelectrolyte adsorption was the amount of the surface anionic charge, whereas surface area appeared to be of less importance. Based on a comparison of solid-liquid and XPS sorption isotherms, different polyelectrolyte conformations were suggested, depending on the types of fines: A flatter conformation and partial cell-wall penetration of polyelectrolytes on kraft fines from freshly prepared pulp, and a more free conformation with extended loops and tails on lignocellulosic fines from recycled pulp. Additionally, ToF-SIMS imaging proved that recycled pulp fines contained residual de-inking chemicals (primarily palmitic acid salts) that possibly hinder the electrostatic interactions with polyelectrolytes. |
| Idioma: | Inglés |