| Título: | EFFECTS OF DYNAMIC AGING (HYDROLYSIS AND CONDENSATION) BEHAVIOUR OF ORGANOFUNCTIONAL SILANES IN THE AQUEOUS SOLUTION ON THEIR PENETRABILITY INTO THE CELL WALLS OF WOOD |
| Autores: |
Xie, Yanjun Hill, Callum A. S. Sun, Dongyang Jalaludin, Zaihan Wang, Qingwen Mai, Carsten |
| Fecha: | 2011-04-29 |
| Publicador: | Bioresources |
| Fuente: |
 |
| Tipo: |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion |
| Tema: | Silane hydrolysis and condensation; Particle size distribution; Penetrability; Cell wall bulking; Equilibrium moisture content; SEM-EDX analysis |
| Descripción: | The hydrolysis and condensation (aging) dynamics of aqueous solutions of (3-glycidyloxypropyl)trimethoxysilane (GPS), vinyltrimethoxysilane (VTS), and (3-aminopropyl)trimethoxysilane (APS) and their penetrability into the cell walls of European spruce (Picea abies) wood were studied to investigate the feasibility of using silanes as a cell wall modifying agent for wood and other lignocellulosic materials. The size distribution of silane particles in aqueous solution was determined using a dynamic light scattering apparatus and increased with the aging time, but at different rates depending on the silane monomer. With increasing aging time, the treated wood exhibited decreased cell wall bulking (swelling), and the water vapour sorption behaviour was less affected by treatments when compared with unmodified wood; SEM-EDX analysis revealed that there was a reduced amount of silane in the cell walls with increased aging time. These findings demonstrate the reduced accessibility of silane to cell walls following aging. |
| Idioma: | Inglés |