| Título: | RECYCLING OF CHEMICAL PULP FROM WHEAT STRAW AND CORN STOVER |
| Autores: |
Tschirner, Urike W. Barsness, James Keeler, Tamara |
| Fecha: | 2007-10-17 |
| Publicador: | Bioresources |
| Fuente: |
 |
| Tipo: |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion |
| Tema: | Wheat, Corn, Recycling strength loss, Crystallinity index, chemical composition |
| Descripción: | Handsheets produced from corn stalks and wheat straw soda AQ pulps were recycled in the lab. Pulping of corn stalks resulted in a low pulp yield, low bonding strength, and low recyclability. Conversely, wheat straw fiber had a better yield, very good tensile properties, and showed a considerably better response to recycling. The tensile index of wheat straw fibers retained 67% of its original value after four cycles. It could be shown that recycling caused only small changes in chemical compo-sition, but that the crystallinity index increased considerably. To be able to understand the behavior of wheat straw fiber as part of a commercial papermaking furnish, a paper containing 20% wheat straw fiber was produced on a 24 inch pilot paper machine and was recycled using a handsheet mold with white water return. Chemical analysis of the control (no wheat fiber) and the wheat-containing paper demonstrated slightly higher xylan content for the wheat-containing material. Recyclability increased slightly with addition of wheat fibers to a commercial furnish. |
| Idioma: | Inglés |